Chemical Micronization of Woody Biomass using the Microwave

극초단파를 이용한 목질 바이오매스의 화학적 분산

Gi-Baek Nah
,
Ji-Ae Ryu
,
Jung-Myoung Lee1
,
Tae-Jin Eom1†
나기백
,
류지애
,
이중명 1
,
엄태진 1†
Department of Wood Science and Technology, Kyungpook National University, Daegu, 41566
1Major in Wood Science and Technology, Department of Wood Science and Technology, School of Forestry, Science and Landscape Architecture, Kyungpook National University, Daegu, 41566
경북대학교 임산공학과
1경북대학교 산림과학·조경학부 임산공학전공
†Corresponding author: E-Mail: tjeom@knu.ac.kr
30 August 2017. pp. 150-158
PDF XML Citation
Abstract

As a basic study for the new materialization of biomass, the chemical dispersion of biomass using microwave was performed under various conditions. And the characteristics of dispersed residues were compared with various conditions. According to the reaction condition of microwave, the residual ratio by chemical micronization of wood meals was decreased, and Klason lignin of residues were also decreased. However, the content of acid soluble lignin did not show any significant difference. These results indicate that the chemical dispersion reaction using microwave showed the lowest residual lignin content at 60 seconds of reaction time and 2.5% of the catalyst condition or at 120 seconds and 2.0%. It is expected that the residual ratio and the residual lignin content can be controlled by the catalyst content and reaction time in the chemical micronization.

Keywords
Chemical micronization
glycol ether
woody biomass
microwave oven
reaction residue
References

Literature Cited

1
A. Kržan and E. Žagar, Bioresource Technology, Microwave driven wood liquefaction with glycols, 100(12); 3143-3146 (2009)

Kržan, A. and Žagar, E., Microwave driven wood liquefaction with glycols, Bioresource Technology 100(12):3143-3146 (2009).

2
S. H. Imam, S. H. Gordon, L. Mao and L. Chen, Polymer Degradation and Stability, Environmentally friendly wood adhesive from renewable plant polymer: Characteristics and optimization, 73(3); 529-533 (2001)

Imam, S. H., Gordon, S. H., Mao, L., and Chen, L., Environmentally friendly wood adhesive from renewable plant polymer: Characteristics and optimization, Polymer Degradation and Stability 73(3):529-533 (2001).

10.1016/s0141-3910(01)00114-8
3
Y. P. Wei, F. Cheng, H. P. Li and J. G. Yu, Journal of Applied Polymer Science, Synthesis and properties of polyurethane resins based on liquefied wood, 92(1); 351-356 (2004)

Wei, Y. P., Cheng, F., Li, H. P., and Yu, J. G., Synthesis and properties of polyurethane resins based on liquefied wood, Journal of Applied Polymer Science 92(1):351-356 (2004).

10.1002/app.20023
4
M. Pääkkö, M. Ankerfors, H. Kosonen, A. Nykänen, S. Ahola, M. Österberg, J. Ruokolainen, J. Laine, P. T. Larsson, O. Ikkala and T. Lindström, Biomacromolecules, Enzymatic hydrolysis combined with mechanical shearing and high pressure homogenization for nanoscale cellulose fibrils and strong gels, 8(6); 1934-1941 (2007)

Pääkkö, M., Ankerfors, M., Kosonen, H., Nykänen, A., Ahola, S., Österberg, M., Ruokolainen, J., Laine, J., Larsson, P. T., Ikkala, O., and Lindström, T., Enzymatic hydrolysis combined with mechanical shearing and high pressure homogenization for nanoscale cellulose fibrils and strong gels, Biomacromolecules 8(6):1934-1941 (2007).

5
E. B. Ahn, S. B. Hong, K. J. Kim and T. J. Eom, Journal of Korea TAPPI, Micro-fibrillated cellulose preparation with enzyme beating pretreatment and effect on paper strength improvement, 47(6); 57-65 (2015)

Ahn, E. B., Hong, S. B., Kim, K. J., and Eom, T. J., Micro-fibrillated cellulose preparation with enzyme beating pretreatment and effect on paper strength improvement, Journal of Korea TAPPI 47(6):57-65 (2015).

10.7584/ktappi.2015.47.6.057
6
C. Yoshida, K. Okabe, T. Yao, N. Shiraishi and A. Oya, Journal of Material Science, Preparation of carbon fibers from biomass-based phenol-formaldehyde resin, 40(2); 335-339 (2005)

Yoshida, C., Okabe, K., Yao, T., Shiraishi, N., and Oya, A., Preparation of carbon fibers from biomass-based phenol-formaldehyde resin, Journal of Material Science 40(2):335-339 (2005).

10.1007/s10853-005-6087-1
7
K. Sudo and K. Shimizu, Journal of Applied Polymer Science, A new carbon fiber from lignin, 44(15); 127-134 (1992)

Sudo, K. and Shimizu, K., A new carbon fiber from lignin, Journal of Applied Polymer Science 44(15):127-134 (1992).

10.1002/app.1992.070440113
8
H. Pan, Z. Zheng and C. Y. Hse, European Journal of Wood and Wood Products, Microwave- assisted liquefaction of wood with polyhydric alcohols and its application in preparation of polyurethane foams, 70(4); 461-470 (2012)

Pan, H., Zheng, Z., and Hse, C. Y., Microwave- assisted liquefaction of wood with polyhydric alcohols and its application in preparation of polyurethane foams, European Journal of Wood and Wood Products 70(4):461-470 (2012).

9
S. H. Lee and T. Ohkita, Wood Science and Technology, Rapid wood liquefaction by supercritical phenol, 37(1); 29-38 (2003)

Lee, S. H. and Ohkita, T., Rapid wood liquefaction by supercritical phenol, Wood Science and Technology 37(1):29-38 (2003).

10.1007/s00226-003-0167-7
10
M. Miura, H. Kagaa, A. Sakuraib, T. Kakuchic and K. Takahashic, Journal of Analytical and Applied Pyrolysis, Rapid pyrolysis of wood block by microwave heating, 71(1); 187-199 (2004)

Miura, M., Kagaa, H., Sakuraib, A., Kakuchic, T., and Takahashic, K., Rapid pyrolysis of wood block by microwave heating, Journal of Analytical and Applied Pyrolysis 71(1):187-199 (2004).

10.1016/s0165-2370(03)00087-1
11
C. O. Kappe, Chemical Society Reviews, Microwave dielectric heating in synthetic organic chemistry, 37; 1127-1139 (2008)

Kappe, C. O., Microwave dielectric heating in synthetic organic chemistry, Chemical Society Reviews 37:1127-1139 (2008).

12
M. J. Gronnow, R. J. White, J. H. Clark and D. J. Macquarrie, Organic Process Research & Development, Energy efficiency in chemical reactions: A comparative study of different reaction techniques, 9(4); 516-518 (2005)

Gronnow, M. J., White, R. J., Clark, J. H., and Macquarrie, D. J., Energy efficiency in chemical reactions: A comparative study of different reaction techniques, Organic Process Research & Development 9(4):516-518 (2005).

10.1021/op0498060
13
O. Mašek, V. Budarin, M. Gronnow, K. Crombie, P. Brownsort, E. Fitzpatrick and P. Hurst, Journal of Analytical and Applied Pyrolysis, Microwave and slow pyrolysis biochar - Comparison of physical and functional properties, 100; 41-48 (2013)

Mašek, O., Budarin, V., Gronnow, M., Crombie, K., Brownsort, P., Fitzpatrick, E., and Hurst, P., Microwave and slow pyrolysis biochar - Comparison of physical and functional properties, Journal of Analytical and Applied Pyrolysis 100:41-48 (2013).

14
K. J. Kim, J. D. Jung, S. E. Jung, S. B. Hong and T. J. Eom, Journal of Korea TAPPI, Delignification of lignocellulosic biomass with high-boiling point solvent and acidic catalyst, 48(1); 119-126 (2016)

Kim, K. J., Jung, J. D., Jung, S. E., Hong, S. B., and Eom, T. J., Delignification of lignocellulosic biomass with high-boiling point solvent and acidic catalyst, Journal of Korea TAPPI 48(1):119-126 (2016).

10.7584/ktappi.2016.48.1.119
15
G. B. Nah, S. E. Jung, S. B. Hong, K. J. Kim, J. M. Lee and T. J. Eom, Chemical dispersion of lignocellulosic materials (LCM) by glycol etherProceeding of Spring Conference of the Korea TAPPI; 87 (2017)

Nah, G. B., Jung, S. E., Hong, S. B., Kim, K. J., Lee, J. M., and Eom, T. J., Chemical dispersion of lignocellulosic materials (LCM) by glycol ether, Proceeding of Spring Conference of the Korea TAPPI, pp. 87 (2017).

16
M. A. Yousef, A. A. Shabaka, A. M. A. Nada and K. N. AbdEl-Nour, Indian Journal of Pure and Applied Physics, Physical properties and IR spectroscopy of thermally treated bagasse paper sheet, 29; 6-8 (1991)

Yousef, M. A., Shabaka, A. A., Nada, A. M. A., and AbdEl-Nour, K. N., Physical properties and IR spectroscopy of thermally treated bagasse paper sheet, Indian Journal of Pure and Applied Physics 29:6-8 (1991).

17
M. G. Alriols, A. Tejado, M. A. Blanco, I. Mondragon and J. Labidi, Chemical Engineering Journal, Agricultural palm oil tree residues as raw material for cellulose, lignin and hemicellulose production by ethylene glycol pulping process, 148(1); 106-114 (2009)

Alriols, M. G., Tejado, A., Blanco, M. A., Mondragon, I., and Labidi, J., Agricultural palm oil tree residues as raw material for cellulose, lignin and hemicellulose production by ethylene glycol pulping process, Chemical Engineering Journal 148(1):106-114 (2009).

10.1016/j.cej.2008.08.008
18
G. Li, C. Hse and T. Qin, Journal of Forestry Research, Wood liquefaction with phenol by microwave heating and FTIR evaluation, 26(4); 1043-1048 (2015)

Li, G., Hse, C., and Qin, T., Wood liquefaction with phenol by microwave heating and FTIR evaluation, Journal of Forestry Research 26(4):1043-1048 (2015).

10.1007/s11676-015-0114-0
19
S. B. Hong, K. J. Kim and T. J. Eom, Journal of Korea TAPPI, Delignification of pine wood meals using high boiling point solvents and acidic catalysts, 48(6); 131-136 (2016)

Hong, S. B., Kim, K. J., and Eom, T. J., Delignification of pine wood meals using high boiling point solvents and acidic catalysts, Journal of Korea TAPPI 48(6):131-136 (2016).

10.7584/jktappi.2016.12.48.6.131
20
K. J. Kim, G. B. Nah, J. A. Ryu and T. J. Eom, Journal of Korea TAPPI, Preparation of lignin rich micro-cellulose fines (LMCFs) by chemical micronization method and characteristics of LMCFs handsheet, 49(3); 109-117 (2017)

Kim, K. J., Nah, G. B., Ryu, J. A., and Eom, T. J., Preparation of lignin rich micro-cellulose fines (LMCFs) by chemical micronization method and characteristics of LMCFs handsheet, Journal of Korea TAPPI 49(3):109-117 (2017).

10.7584/jktappi.2017.06.49.3.109
21
J. M. Lawther, R. Sun and W. B. Bank, Journal of Agricultural and Food Chemistry, Fractional characterization of wheat straw lignin components by alkaline nitrobenzene oxidation and FT-IR spectroscopy, 44(5); 1241-1247 (1996)

Lawther, J. M., Sun, R., and Bank, W. B., Fractional characterization of wheat straw lignin components by alkaline nitrobenzene oxidation and FT-IR spectroscopy, Journal of Agricultural and Food Chemistry 44(5):1241-1247 (1996).

10.1021/jf9502764
22
Y. Huang, L. Wang, Y. Chao, D. S. Nawawi, T. Akiyama, T. Yokoyama and Y. Matsumoto, Journal of Wood Chemistry and Technology, Analysis of lignin aromatic structure in wood based on the IR spectrum, 32(4); 294-303 (2012)

Huang, Y., Wang, L., Chao, Y., Nawawi, D. S., Akiyama, T., Yokoyama, T., and Matsumoto, Y., Analysis of lignin aromatic structure in wood based on the IR spectrum, Journal of Wood Chemistry and Technology 32(4):294-303 (2012).

10.1080/02773813.2012.666316
23
X. Colom, F. Carrillo, F. Nogués and P. Garriga, Polymer Degradation and Stability, Structural analysis of photodegraded wood by means of FTIR spectroscopy, 80(3); 534-549 (2003)

Colom, X., Carrillo, F., Nogués, F., and Garriga, P., Structural analysis of photodegraded wood by means of FTIR spectroscopy, Polymer Degradation and Stability 80(3):534-549 (2003).

10.1016/s0141-3910(03)00051-x
24
M. L. Nelson and R. T. O’Connor, Part I: Spectra of Lattice type I, II, III and of amorphous cellulose, Journal of Applied Polymer Science, Relation of certain infrared bands to cellulose crystallinity and crystal Lattice type, 8(3); 1311-1324 (1964)

Nelson, M. L. and O’Connor, R. T., Relation of certain infrared bands to cellulose crystallinity and crystal Lattice type, Part I: Spectra of Lattice type I, II, III and of amorphous cellulose, Journal of Applied Polymer Science 8(3):1311-1324 (1964).

Information
  • Publisher :Korea Technical Association of The Pulp and Paper Industry
  • Publisher(Ko) :한국펄프종이공학회
  • Journal Title :Journal of Korea TAPPI
  • Journal Title(Ko) :펄프종이기술
  • Volume : 49
  • No :4
  • Pages :150-158
  • Received Date : 2017-08-06
  • Revised Date : 2017-08-16
  • Accepted Date : 2017-08-18
  • DOI :https://doi.org/10.7584/JKTAPPI.2017.08.49.4.150
Journal Informaiton Journal of Korea TAPPI Journal of Korea TAPPI
Online Submission
  • scopus
  • NRF
  • KOFST
  • crossref crossmark
  • crossref cited-by
  • crosscheck
  • orcid
Journal Informaiton Journal Informaiton - close